Non-ferrous Metal Materials and product

Size: M2-M64
Standard: DIN125 DIN127
Material: GR1/GR2/GR3/GR5
Surface Treatment: Anodizing, polishing,black oxide
Advantage: OEM / customized service provided
Application: Industry; medical; car; motorcycles; bicycles
Feature: Protection connection; corrosion resistance; low density

Titanium Grade: Gr2 / Gr7
Size: Customized as your drawing or sample request
Features: Acid and alkali resistance, anti-corrosion, excellent mechanical strength etc.
Applications: Home Improvement, Sport Equipments, Motocycle DIY, Frames, Disc Brakes, Fasteners, Pipes, Car and Bicycle Modification
Surface treatment: Polished,Anodizing, Black oxide

Purity: 99.95% min
Grade: R05200, R05400, R05252, RO5255, R05240
Standard : ASTM B365
Size: Dia(1~25)xMax3000mm
Condition
1.Hot-rolled/Cold-rolled
2.Alkaline Cleaning
3.Electrolytic Polish
4.Machining, grinding
5.Stress relief annealing

Material: 99.6% tantalum
Color: nickel white
Standard: ASTM B365 ASTM B780
Grade: R05400 R05200, R05252, R05255, R05240
Length: 3.0mm~150mm
Features: Good ductility and toughness , Low coefficient of thermal expansion, Good corrosion resistance
Used: Electrical industry, tool bit and aiguille, modern medicine, metallurgy, aviation.

Appearance：Silver white
Shape： Granular
Model Standard：ASTM Standard
Application：Magnesium is an indispensable non-ferrous metal powder in the current high-tech field, which is widely used in aviation, aerospace, automobile, petroleum, chemical industry, medicine, metallurgy and other industries.

Magnesium Specification: AZ91D ,AM50A , AM60B
Size (mm): 1.2*1.2*4
Magnesium Nanoparticles Mg APS: 20-300mesh
Magnesium Nanoparticles Mg Purity: 99.9% (metal basis)
Magnesium Nanoparticles Mg Morphology: spherical
Magnesium Nanoparticles SSA: 2.5 - 5m2/g
Magnesium Melting point/Melting range: 650°C
Magnesium Boiling point/Boiling range: 1100°C
Magnesium Density at 20°C: 1.738 g/cm³

Shape: Round
Standard：AMS/ASTM/JIS/BS/ISO
Brand：AZ31B/ZK60A/AZ91D/AZ61A/AZ40M/AZ80A
Dimension：φ3-φ130mm*3000mm(Customized)

Size Range: Sheet: thickness from 0.5mm to 7mm; Max. width is 600mm; Max. length is 1200mm;
Chemical Composition: Al: 2.5-3.5%; Zn: 0.7-1.3%; Mn: 0.20 – 1.0%; Mg: Balance
Physical Properties:
Density: 1.78g/cm3
Coefficient of thermal expansion: 26.8 x 10-6K-1
Specific heat: 1040 Jkg-1k-1
Thermal conductivity: 76.9Wm-1k-1
Electrical resistivity: 92nΩm
Modulus of elasticity: 45 x 109Pa
Poissons ratio: 0.35
Melting range: 566 - 632°C

Material: Mo1,Mo2,TZM
Standard: ASTMB386, GB/T 3877
Application: Construction of furnace tooling and parts and as a feed stock for the fabrication of parts for the electronics and semiconductor industries.
Processing: Powdering, molding, sintering,machining
Feature: High strength, long service life, good flatness
Surface: Polishing/ground, caustic washing

Purity Nb: ≥99.95%
Density :8.57g/cc
Specification range: As per customer request
Surface: Black or bright
Property :Superconductivity, corrision resistance, wear resistance, high melting point, ductility, paramagnetism etc.
Usage: Steel industry, superconductor materials, aerospace, atomic energy industry
Standard: ASTM B393
Certificate: ISO 9001;2015

Material: Nickel
Dimensions: 300 mm X 200 mm or customized
Thickness: 0.3 mm or customized
Net weight: ~4 g
Surface density: 320 g/m2
Porosity: 97%, 110 pores per inch (110 PPI)
Pore size: ~0.25 mm
Longitudinal tensile strength ≥95 N/cm2
Longitudinal elongation ≥ 5%
Transverse tensile strength ≥60 N/cm2
Transverse elongation ≥ 10%

Material: N4/ Ni 201 N6/ Ni 200
Standard: ASTM B161 ASTM B163 ASTM B165 GB/T2882-2005
Size: Diameter 6.0~150mm * Long 6000mm max, wall thickness 0.8 ~ 8.0mm
Technique: Forged Hot rolling machine Cold rolling machine Polish
Status: Hot rolled, Cold rolled, Annealed(according to the user's requirements, special specifications and user standards)